Furthermore, the blockage is rarely pure sludge. It is a composite material: magnetite particles bind with limescale (calcium carbonate) in hard water areas and with flux residues left over from the original installation. When a system is repeatedly turned on and off, the sludge undergoes thermal cycling, hardening into a cement-like substance known as “copper carbonate” or simply “hard sludge.” This metamorphosis transforms a removable deposit into a near-permanent obstruction that can withstand pressures of up to 3 bar.
To understand the blockage, one must first understand the medium. Central heating water is not inert; it is a reactive chemical soup. Over time, the interaction between ferrous radiators (steel or cast iron) and copper pipework creates a galvanic cell, leading to corrosion. The byproduct of this corrosion is magnetite (Fe₃O₄), a black, sludgy substance. In a standard 22mm system, this sludge often settles in the lower loops of radiators, causing cold spots but rarely stopping flow entirely. In a microbore system, however, the pipe’s internal diameter is often a mere 6mm to 8mm. A 1mm build-up of magnetite reduces the cross-sectional area by over 40%. A 2mm build-up constitutes a complete occlusion. microbore central heating blockage
Diagnosing a microbore blockage requires eliminating other variables. The first step is the magnet test : sliding a strong neodymium magnet along the microbore pipe. A sudden “stick” indicates a high concentration of magnetite. The second is thermal imaging , which reveals a sharp temperature gradient at the precise point of occlusion. Unlike a standard system where blockages are typically in radiators, microbore blockages are perversely located in the 6mm branches between the manifold (a central distribution hub) and the radiator valves. Furthermore, the blockage is rarely pure sludge
Recent Comments